Major Features 主要優點
Long open time 操作時間長
High shear and peel strength 高的剪切與高剝離強度
Excellent low temperature properties 優異的低溫性能
Room temperature cure 常溫固化
Controlled flow 流動性容易控制
PROPERTIES OF UNCURED MATERIAL 固化前材料性能
|
Property性能
|
Test Method測試方法
|
800A
|
800B
|
|
Color/appearance
顏色
|
Visual
目視
|
Creamy white, viscous/liquid
膏狀白色粘稠液體
|
Amber Liquid
琥珀色液體
|
|
SpecificGrav密度, g/cc
|
ASTM D-792
|
1.12
|
1.10
|
|
Viscosity粘度(cP), 25ºC
|
ASTM D-2393
|
60,000 - 100,000
|
8,000 - 12,000
|
TYPICAL CURED PROPERTIES 固化后屬性
|
Property
性能
|
Test Method
測試方法
|
Test Value
測試值
|
|
Hardness, casting after 15 minutes, Shore D 邵氏硬度，澆鑄15分鐘后
|
D-2240
|
75
|
|
Ultimate Tensile Strength
極限抗張強度, psi
|
D-638
|
5200
|
|
Elongation 生長率, %
|
D-638
|
7
|
|
Modulus 模量(psi)
|
D-638
|
400, 000
|
|
T- Peel Test 剝離測試(pli)
|
D-1876
|
50-60
|
|
Lap shear strength 搭接剪切強度, psi at 25C
|
ASTM D-1002
|
|
|
Galvanized Steel 鍍鋅鋼
|
|
2500
|
|
Fibre reinforced composite 纖維增強復合材料
|
|
1500
|
|
Mineral filled PET plastics 礦物填充PET塑料
|
|
800
|
|
Aluminum (primered) 鋁
|
|
5000
|
|
Aluminum (acid etched) 鋁（酸腐蝕）
|
|
4200
|
Effects of application temperature on lap shear strength(LSS ) by ASTM D-1002
溫度對搭接剪切的影響
Load applied 10 minutes after specimens reach test temperature當樣品達到測試溫度后10分鐘
|
|
Test Temperature
|
LSS Value, psi
|
|
Al/Al
|
-60ºC
|
4700
|
|
Al/Al
|
82 ºC
|
1500
|
|
Al/Al
|
121 ºC
|
500
|
|
Al/Al
|
30 days salt spray
|
4000
|
|
Al/Al
|
30 days @ 60ºC/100% RH
|
3500
|
Directions for use使用方法
|
Reaction Ratio (by weight) 反應重量比
|
|
100A/49B
|
|
Reaction Ratio (by volume) 反應體積比
|
|
100A/50B
|
|
Pot Life (100 grams) 25°C 使用時間（100克）
|
ASTM D-2471
|
30 minutes
|
|
Pot Life (20 grams) 25°C 使用時間（20克）
|
|
60 minutes
|
Curing time table固化進度表:
3-5 days at 77?F. or elevated temperatures for accelerated cure. 在25攝氏度下3-5天。或者在升高的溫度下
加速固化
Shelf Life 保質期
Provided this material is stored under the recommended storage condition in the original container, it will remain in useable condition for
from date of shipping.
若該產品按照上述要求存儲，并且是保存在原裝容器內，從發貨之日起，在一年內可以使用。